First Scientific Testing
at the University of Nevada, Reno
|
The first independent testing laboratory selected was the University
of Nevada, Reno (UNR). UNR was chosen because it is a fully accredited,
125 year old University, assuring creditability and impartiality. The
following is the summary of 2 tests performed at the University of Nevada,
Reno:
“ATTENTION: ROBERT MURPHY-PRESIDENT/CEO.
SUBJECT: SUMMARY OF 2 TESTS ON YOUR CORROSION
PROTECTION COMPOUND.
Dear Mr. Murphy,
|
|
Reference the above and the sample sent to me for
testing the corrosion protection of the above compound as compared
to Rustoleum.
Summary of Expt. #1:
Two stainless steel rods were sprayed with Rustoleum and coated
with your compound, dried for 12 hours at 20 degrees C, and then immersed
in hydrochloric acid, approximately 5% by weight.
After immersing the same for 8.5 hours, at room temperature,
the Rustoleum coating peeled off, whereas your compound’s coating
remained intact.
CONCLUSION:
YOUR COMPOUND WORKS BETTER THAN RUSTOLEUM.
|
Rod #1 is coated with Rust-oleum®,
Rod #2 is coated with Rust Bullet® |
|
Summary of Expt. #2:
Three identical six inch long black iron nipples were
sanded, washed and dried, then immersed in about 10% hydrochloric acid.
The first nipple was sanded and immersed in the acid as-is, whereas
the second nipple was coated, twice, with Rustoleum and the third nipple
was coated with your product.
The nipples were dried, two with the coatings, for two hours
and 26 minutes at 30 degrees C, thereafter the nipples were immersed
in the above acid, SG of 1.052.
After four hours, the Rustoleum was peeling, whereas
your compound was intact.
|
Nipple #1 is the Control Nipple,
Nipple #2 is two coats of Rust-oleum®,
Nipple #3 is one coat of Rust Bullet®
|
|
After 6 hours and 20 minutes, Rustoleum was completely removed,
whereas the as-is nipple showed normal corrosion and your product’s
coating was intact.
After 16 hours and 27 minutes your coating was still intact,
whereas, the Rustoleum was long gone, as above, and the as-is showed
accelerated acid corrosion.
CONCLUSION:
YOUR COMPOUND WORKS BETTER THAN RUSTOLEUM.
A formal report with photographs will be sent to you this week.
Sincerely,
(Signature)
Mobashir N. Ahmad
Proprietor
Chemicals & Metals, Inc.
Environmental and Metallurgical Consultant
C/O
University of Nevada at Reno
MS 199
Reno, Nevada 89557”
“To
view original UNR Report in PDF format click here”
“To
view full formal UNR Report click here”
|
|
|
|
|
|
|