First Scientific Testing
at the University of Nevada, Reno

The first independent testing laboratory selected was the University of Nevada, Reno (UNR). UNR was chosen because it is a fully accredited, 125 year old University, assuring creditability and impartiality.

The following is the summary of 2 tests performed at the University of Nevada, Reno:

“ATTENTION: ROBERT MURPHY-PRESIDENT/CEO.

SUBJECT: SUMMARY OF 2 TESTS ON YOUR CORROSION
PROTECTION COMPOUND.

Dear Mr. Murphy,

Reference the above and the sample sent to me for testing the
corrosion protection of the above compound as compared to
Rustoleum.

Summary of Expt. #1:
Two stainless steel rods were sprayed with Rustoleum and coated with your compound, dried for 12 hours at 20 degrees C, and then immersed in hydrochloric acid, approximately 5% by weight.

After immersing the same for 8.5 hours, at room temperature, the Rustoleum coating peeled off, whereas your compound’s coating remained intact.

CONCLUSION:
YOUR COMPOUND WORKS BETTER THAN RUSTOLEUM.
Rust Preventatives
Rod #1 is coated with Rust-oleum®,
Rod #2 is coated with Rust Bullet®

Summary of Expt. #2:
Three identical six inch long black iron nipples were sanded, washed and dried, then immersed in about 10% hydrochloric acid.

The first nipple was sanded and immersed in the acid as-is, whereas the second nipple was coated, twice, with Rustoleum and the third nipple was coated with your product.

The nipples were dried, two with the coatings, for two hours and 26 minutes at 30 degrees C, thereafter the nipples were immersed in the above acid, SG of 1.052.

After four hours, the Rustoleum was peeling, whereas your compound was intact.

Rust prevention
Nipple #1 is the Control Nipple,
Nipple #2 is two coats of Rust-oleum®,
Nipple #3 is one coat of Rust Bullet®


After 6 hours and 20 minutes, Rustoleum was completely removed, whereas the as-is nipple showed normal corrosion and your product’s coating was intact.

After 16 hours and 27 minutes your coating was still intact, whereas, the Rustoleum was long gone, as above, and the as-is showed accelerated acid corrosion.

CONCLUSION:
YOUR COMPOUND WORKS BETTER THAN RUSTOLEUM.
A formal report with photographs will be sent to you this week.

Sincerely,

(Signature)

Mobashir N. Ahmad
Proprietor
Chemicals & Metals, Inc.
Environmental and Metallurgical Consultant
C/O
University of Nevada at Reno
MS 199
Reno, Nevada 89557”

“To view original UNR Report in PDF format click here”
“To view full formal UNR Report click here”

The requirements for testing Rust Bullet® became so in-depth that UNR could not provide some of the sophisticated equipment necessary to perform the corrosion control products testing; therefore, three additional accredited independent laboratories, specializing in the type of scientific testing Rust Bullet® required, were sought out...

Click on photos to view our other scientific testing programs

National Testing
Standards, Inc.
University of Nevada, Reno
 Corrosion Preventatives
Rust Prevention products
Q-Labs Weathering
Research Center
 Rust Corrosion prevention
Our on going Real-Time Environmental Exposure Testing
Rust Corrosion inhibitors rust preventative

All trademarks and copyrights are owned by their respective owners.


Rust Bullet - Rust Bullet Application - About Rust Bullet
How Rust Bullet Works - Rust Bullet FAQ
POR15® and >Wasser® Brand System Comparison - MSDS Data
Corrosion Engineering Data - Home and Farm Uses
Commercial Uses - Car Rust Prevention - Rust Resources

Rust Bullet, LLC ©2002 - 2004 All rights reserved.